| 1. | Composite layering control circuit 图案重迭控制电路 |
| 2. | Preparating technique of nanocermet composite layer with method of ultrasonic - electrodepositing 超声电沉积制备纳米金属陶瓷复合镀层工艺 |
| 3. | The composite layered architecture of an soa can leverage existing systems and integrate them using service - oriented integration techniques Soa的复合层架构可以利用现有的系统并且用基于服务的集成技术来集成它们。 |
| 4. | With the correct compound designing , a composite layer with thickness of 1 . 5to 6 millimeters was formed on the surface of casting by means of cast - sintering technique 通过合理的成分设计和工艺参数的优化选择,利用铸造烧结技术,在铸铁件表面获得了一层厚为1 . 5 6mm的耐磨复合材料层。 |
| 5. | Martensite and austenitic form the matrix of the composite . ( cr , fe ) 7c3 is also a kind of reinforcement . ( 3 ) the combine of the composite layer and master - alloy is metallurgic combination and has a very high combining - intensity ( 2 )表面复合层内增强相tic或vc为原位生成,其颗粒细小,分布均匀,无明显梯度分布或偏聚现象。 |
| 6. | Because of laser ' s transient heating and fast cooling on metal surface , laser cladding ceramic reinforced composite layer on titanium alloy surface can greatly improve wear resistance of titanium alloy 利用高能激光束对材料表面瞬间加热和熔池快速冷却的特性,在钛合金表面用激光熔覆一层陶瓷增强复合材料,能够显著提高钛合金的耐磨性能。 |
| 7. | The experimental result of the abrasive wear resistance shows that when the volume percentage of wc particles presented in the layer is about 38 % , the composite layer has the best wear - resistance which is better than the high - cr cast iron 试验结果表明:复合层中保持38 %左右的wc颗粒,其耐磨粒磨损性能最佳,明显高于高铬铸铁,所以这种复合材料具有广阔的应用前景。 |
| 8. | Then , the fluid was coated on the surface of c / c composite dental implants , a stronger modified composites layer was formed on the surface of c / c composites by means of heat treatment at 1 100 研究结果表明:在热固性酚醛树脂中添加10 % 25 %的羟磷灰石细粉制成浆体,用预氧丝作增强剂包覆于炭炭复合材料牙种植体表面,再经1100高温处理,可以在炭炭复合材料的表面形成强度良好的复合改性膜。 |
| 9. | The result of those studies as follow : ( 1 ) an composite layer of definite thickness on the casting was gained by cast - sintering technique , and it has well wear - resistance . ( 2 ) the reinforcement of the composite layer is tic or vc , which was exiguous and is well distributed 同时利用干滑动摩擦磨损实验,对表面复合层的耐干滑动摩擦磨损的性能进行了研究。研究表明: ( 1 )利用铸造烧结技术可以在铸件表面获得一定厚度耐磨性能良好的表面复合层。 |
| 10. | This layer is combined with the matrix metallurgically . for the wc particles of the layer , the coaser the wc particle is , the higher the radio is , and the worse the composite layer is . the optimum size of wc particles is about 70 ~ 150 mesh , and the optimum volume percentage of wc particles is about 25 ~ 40 % 复合层中的wc颗粒越粗化,所占比例越多,对复合层与母材结合越不利,试验得知wc的粒度为70 ~ 150目,体积分数为25 ~ 40 %时,复合层结合良好。 |